PA66 DP 2325 H3.0 000000德國朗盛Durethan耐熱老化耐沖擊尼龍66塑料（18024445500）

PA 66, non-reinforced, injection molding, improved impact strength, heat-aging stabilized



ISO Shortname: ISO 1874-PA 66-HI, GHR, 14-020

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
Molding shrinkage, parallel 150x105x3; 280 °C / MT 80 °C; 500 bar % acc. ISO 2577 2.1　
Molding shrinkage, transverse 150x105x3; 280 °C / MT 80 °C; 500 bar % acc. ISO 2577 1.9　
Post- shrinkage, parallel 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.5　
Post- shrinkage, transverse 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.1　
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 2.1　
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 1.6　
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.5　
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.2　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 1800 700
C Yield stress 50 mm/min MPa ISO 527-1,-2 50 30
C Yield strain 50 mm/min % ISO 527-1,-2 21 38
C Nominal strain at break 50 mm/min % ISO 527-1,-2 50 50
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 47 49
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 80 290
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU N N
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU N N
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 50 100
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA 20 20
Izod impact strength 23 °C kJ/m² ISO 180-1U N N
Izod impact strength -30 °C kJ/m² ISO 180-1U N N
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 80 100
Izod notched impact strength -30 °C kJ/m² ISO 180-1A 25 20
Flexural modulus 2 mm/min MPa ISO 178-A 1700 660
Flexural strength 2 mm/min MPa ISO 178-A 70 27
Flexural strain at flexural strength 2 mm/min % ISO 178-A 7.2 8.7
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 55 19
C Puncture maximum force 23 °C N ISO 6603-2 3900　
C Puncture maximum force -30 °C N ISO 6603-2 5400　
C Puncture energy 23 °C J ISO 6603-2 50　
C Puncture energy -30 °C J ISO 6603-2 60　

Thermal properties
C Melting temperature 10 °C/min °C ISO 11357-1,-3 263　
C Temperature of deflection under load 1.80 MPa °C ISO 75-1,-2 60　
C Temperature of deflection under load 0.45 MPa °C ISO 75-1,-2 110　
C Temperature of deflection under load 8.00 MPa °C ISO 75-1,-2 50　
Vicat softening temperature 50 N; 120 °C/h °C ISO 306 > 200　
C Coefficient of linear thermal expansion, parallel 23 to 55 °C 10-4/K ISO 11359-1,-2 1.3　
C Coefficient of linear thermal expansion, transverse 23 to 55 °C 10-4/K ISO 11359-1,-2 1.3　
C Burning behavior UL 94 (1.6 mm) 1.6 mm Class UL 94 HB　
Burning behavior UL 94 3.2 mm Class UL 94 HB　
C Oxygen index Method A % ISO 4589-2 20　
Glow wire test (GWFI) 2.0 mm °C IEC 60695-2-12 650　
Burning behavior US-FMVSS302 >=1.0 mm　ISO 3795 25　
C Vicat softening temperature 50 N; 50 °C/h °C ISO 306 > 200　

Electrical properties (23 °C/50 % r. h.)
C Relative permittivity 100 Hz - IEC 60250 3.5 7.0
C Relative permittivity 1 MHz - IEC 60250 3.0 3.4
C Dissipation factor 100 Hz 10-4 IEC 60250 80 1500
C Dissipation factor 1 MHz 10-4 IEC 60250 150 750
C Volume resistivity　Ohm·m IEC 60093 1E17 1E15
C Surface resistivity　Ohm IEC 60093 1E15 1E14
C Electric strength 1 mm kV/mm IEC 60243-1 40 45
C Comparative tracking index CTI Solution A V IEC 60112 600　

Other properties (23 °C)
C Water absorption (Saturation value) Water at 23 °C % ISO 62 7.0　
C Water absorption (Equilibrium value) 23 °C; 50 % RH % ISO 62 2.0　
C Density　kg/m³ ISO 1183 1076　

Processing conditions for test specimens
C Injection molding-Melt temperature　°C ISO 294 280　
C Injection molding-Mold temperature　°C ISO 294 80　

Processing recommendations
Drying temperature dry air dryer　°C - 80　
Drying time dry air dryer　h - 2-6　
Residual moisture content　% Acc. to Karl Fischer　0.03-0.12　
Melt temperature (Tmin - Tmax)　°C - 270-290　
Mold temperature　°C - 80-100　

C These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.