PA6 BKV 60 EF DUS097 000000德國朗盛Durethan 60%玻纖增強尼龍6塑料（18024445500）

PA 6, 60 % glass fibers, injection molding, improved flowability, heat-aging stabilized



ISO Shortname: ISO 1874-PA 6, GHR, 10-190, GF60

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.3　
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.6　
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.03　
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.02　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 19400 12500
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 230 158
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 2.5 3.5
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 95 95
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 17 24
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA 17　
Izod impact strength 23 °C kJ/m² ISO 180-1U 90 90
Izod impact strength -30 °C kJ/m² ISO 180-1U 95 95
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 18 29
Izod notched impact strength -30 °C kJ/m² ISO 180-1A 18　
Flexural modulus 2 mm/min MPa ISO 178-A 20000 13600
Flexural strength 2 mm/min MPa ISO 178-A 390 260
Flexural strain at flexural strength 2 mm/min % ISO 178-A 3 4
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A　250
C Puncture maximum force 23 °C N ISO 6603-2 1476　
C Puncture maximum force -30 °C N ISO 6603-2 1346　
C Puncture energy 23 °C J ISO 6603-2 4.3　
C Puncture energy -30 °C J ISO 6603-2 3.8　

Thermal properties
C Melting temperature 10 °C/min °C ISO 11357-1,-3 221　
C Temperature of deflection under load 1.80 MPa °C ISO 75-1,-2 213　
C Temperature of deflection under load 0.45 MPa °C ISO 75-1,-2 220　
C Temperature of deflection under load 8.00 MPa °C ISO 75-1,-2 186　
C Coefficient of linear thermal expansion, parallel 23 to 55 °C 10-4/K ISO 11359-1,-2 0.1　
C Coefficient of linear thermal expansion, transverse 23 to 55 °C 10-4/K ISO 11359-1,-2 0.8　

Other properties (23 °C)
C Water absorption (Saturation value) Water at 23 °C % ISO 62 3.75　
C Water absorption (Equilibrium value) 23 °C; 50 % RH % ISO 62 1.18　

Processing conditions for test specimens
C Injection molding-Melt temperature　°C ISO 294 280　
C Injection molding-Mold temperature　°C ISO 294 80　

Processing recommendations
Drying temperature dry air dryer　°C - 80　
Drying time dry air dryer　h - 2-6　
Residual moisture content　% Acc. to Karl Fischer　0.06-0.20　
Melt temperature (Tmin - Tmax)　°C - 270-290　
Mold temperature　°C - 80-120　

C These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.