PA6 BKV 330 H2.0 901510德國朗盛Durethan 30%玻纖增強(qiáng)焊接功能改善尼龍6塑料（18024445500）

PA 6, 30 % glass fibers, injection molding, improved weldability



ISO Shortname: ISO 1874-PA 6, GHR, 14-100, GF30

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.35　
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.7　
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.06　
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.07　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 9800 5600
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 170 100
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.0 8.0
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 80 95
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 65 65
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 12 20
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA < 10 < 10
Izod impact strength 23 °C kJ/m² ISO 180-1U 75 85
Izod impact strength -30 °C kJ/m² ISO 180-1U 75 70
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 12 < 10
Izod notched impact strength -30 °C kJ/m² ISO 180-1A <10　
Flexural modulus 2 mm/min MPa ISO 178-A 8300 4900
Flexural strength 2 mm/min MPa ISO 178-A 260 150
Flexural strain at flexural strength 2 mm/min % ISO 178-A 4.5 7.0
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 245 120
C Puncture maximum force 23 °C N ISO 6603-2 883　
C Puncture maximum force -30 °C N ISO 6603-2 791　
C Puncture energy 23 °C J ISO 6603-2 3.4　
C Puncture energy -30 °C J ISO 6603-2 2.8　
Ball indentation hardness　N/mm² ISO 2039-1 195 95

Thermal properties
C Melting temperature 10 °C/min °C ISO 11357-1,-3 222　
C Temperature of deflection under load 1.80 MPa °C ISO 75-1,-2 200　
C Temperature of deflection under load 0.45 MPa °C ISO 75-1,-2 215　
C Temperature of deflection under load 8.00 MPa °C ISO 75-1,-2 90　
Vicat softening temperature 50 N; 120 °C/h °C ISO 306 > 200　
C Coefficient of linear thermal expansion, parallel 23 to 55 °C 10-4/K ISO 11359-1,-2 0.2　
C Coefficient of linear thermal expansion, transverse 23 to 55 °C 10-4/K ISO 11359-1,-2 1.0　
C Burning behavior UL 94 (1.6 mm) 1.6 mm Class UL 94 HB　
Burning behavior UL 94 3.2 mm Class UL 94 HB　
C Oxygen index Method A % ISO 4589-2 23　
Glow wire test (GWFI) 2.0 mm °C IEC 60695-2-12 700　
Burning behavior US-FMVSS302　 ISO 3795 passed　
C Vicat softening temperature 50 N; 50 °C/h °C ISO 306 > 200　

Electrical properties (23 °C/50 % r. h.)
C Relative permittivity 100 Hz - IEC 60250 4.5 17
C Relative permittivity 1 MHz - IEC 60250 3.9 4.8
C Dissipation factor 100 Hz 10-4 IEC 60250 190 3900
C Volume resistivity　Ohm·m IEC 60093 1E13 1.7E13
C Surface resistivity　Ohm IEC 60093 1E13 3.6E13
C Electric strength 1 mm kV/mm IEC 60243-1 32　
C Comparative tracking index CTI Solution A V IEC 60112 450　

Other properties (23 °C)
C Water absorption (Saturation value) Water at 23 °C % ISO 62 6.5　
C Water absorption (Equilibrium value) 23 °C; 50 % RH % ISO 62 2.3　
C Density　kg/m³ ISO 1183 1360　
Bulk density　kg/m³ ISO 60 700　

Processing conditions for test specimens
C Injection molding-Melt temperature　°C ISO 294 280　
C Injection molding-Mold temperature　°C ISO 294 80　

Processing recommendations
Drying temperature dry air dryer　°C - 80　
Drying time dry air dryer　h - 2-6　
Residual moisture content　% Acc. to Karl Fischer　0.03-0.12　
Melt temperature (Tmin - Tmax)　°C - 270-290　
Mold temperature　°C - 80-120　

C These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.