PA6 BKV 30 N1 000000德國(guó)朗盛Durethan 30%玻纖增強(qiáng)阻燃注塑級(jí)尼龍6塑料（18024445500）

PA 6, 30 % glass fibers, injection molding, flame retardant



ISO Shortname: ISO 1874-PA 6, GFR, 14-120, GF30; ISO1043-PA GF FR (22)

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.22　
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.60　
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.04　
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.12　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 11700 6500
C Yield stress 50 mm/min MPa ISO 527-1,-2　80
C Yield strain 50 mm/min % ISO 527-1,-2　3.5
C Nominal strain at break 50 mm/min % ISO 527-1,-2　4.0
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 140 80
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 2.0 3.6
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 60 55
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 60 45
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 12 12
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA < 10 < 10
Charpy notched impact strength -40 °C kJ/m² ISO 179-1eA < 10 < 10
Izod impact strength　kJ/m² ISO 180-1U 50 45
Izod notched impact strength -30 °C kJ/m² ISO 180-1A < 10 < 10
Izod notched impact strength -40 °C kJ/m² ISO 180-1A < 10 < 10
Flexural modulus 2 mm/min MPa ISO 178-A 11000 7500
Flexural strength 2 mm/min MPa ISO 178-A 230 145
Flexural strain at flexural strength 2 mm/min % ISO 178-A 2.5 3.5
C Puncture energy 23 °C J ISO 6603-2 7 9
C Puncture energy -30 °C J ISO 6603-2 5